The combination of polybutylene terephthalate (PBT) and polyamide 6 (PA6) plastic mixture was taken from waste from the table production process along with carbon black (CB) reinforcement with the desire to create a potential plastic mixture widely used in many fields. The PBT/PA6/CB mix is created by injection molding with a CB weight ratio of 0%, 4%, 8%, and 12%. This study has shown the change in plastic’s mechanical properties when adding CB to the mixture by testing the unnotched impact toughness according to ASTM D256 standards. Research results show that the unnotched impact toughness was gradually reduced when increasing the CB content in the mixture from 0% to 12% CB. Specifically, at 0% CB, the resulting unnotched impact toughness was 12.85 kJ/m², reduced to 4.78 kJ/m².

In this paper, the characteristic behavior of the disc consisting of thermoplastic composite CF/PA6 material was considered. Analysis was made by taking into account the usage areas of the materials and referring to certain temperatures between 30 ℃ and 150 ℃. Composite materials are lightweight; they show high strength. For these reasons, they are preferred in technology, especially in the aircraft and aerospace industry. With this study, the radial and tangential stresses determined within a certain temperature The temperatures were determined and compared with previous studies in the literature. According to the results obtained, it is believed that the thermoplastic composite CF/PA6 disc design can be used in engineering.