The electrospinning precursor solution was prepared by dissolving polyvinyl pyrrolidone as template, tetrabutyl titanate as titanium source, and acetic acid as inhibitor. The TiO₂ nanofilms were prepared by precursor solution electrospinning and subsequent calcination. Thermal gravimetric analysis (TG), scanning electron microscopy (SEM), X-ray powder diffraction (XRD), and transmission electron microscopy (TEM) were used to characterize and analyze the samples. The influence of technological parameters on spinning fiber morphology was also studied. The results indicate that the TiO₂ nanofibers morphology is good when the parameters are as follows: voltage 1.4×10⁴ V，spinning distance 0.2 m，translational velocity 2.5×10^-3 m·s^-1, flow rate 3×10^-4 m·s^-1, and needle diameter 3×10^-4 m. The diameter of the fibers is about 150 nm. With the 1×10^-4 mol·L^-1 methylene blue solution used as simulated degradation target, the degradation rate is 95.8% after 180 minutes.

Electrospinning nanofiber membrane has the advantages of wide raw materials, large specific surface area, and high porosity. It is an ideal separator material for lithium-ion batteries. This paper first introduces two common electrospinning nanofiber diaphragms: polymer, polymer, and inorganic composite, and then focuses on the modification methods of composite modification, blending modification, and inorganic modification, as well as the methods of electrospinning nano modified polyolefin diaphragm. Finally, the development direction of the electrospinning lithium-ion battery separator has prospected.

The search for the development of nanostructured materials has led to the study of the properties of their precursors. For the production of nanofibers by the electrospinning process, it is necessary to determine the rheological parameters of the precursor solutions. Since these properties can be influenced by the processing variables and chemical composition of the polymer, this study aims to elucidate the effect of the addition of vinyl monomers in the formulation of nanofibers based on polyacrylonitrile and to determine the optimal parameters for the production of the precursor polymer solution. The effects of temperature and addition of vinyl monomers were evaluated by rheometry, from the analysis of the variation of the viscosity of the solutions, and by microscopy, the morphology of the nanofibers produced. It was observed that the increase in the temperature used to produce the solutions improves the fibers’ properties. Still, there is a relationship between the time of exposure of the polymeric solution to the temperature and the homogeneity of the fibers, which cannot exceed 45 min. The addition of vinyl monomers, to produce PAN-PVA co-polymeric fibers, increases the conductivity and reduces the viscosity of the solutions, resulting in more refined and homogeneous fibers.