Synthesis of macro-mesoporous Titania (Titanium dioxide-TiO₂) nanospheres was successfully achieved using a modified template-free methodology to incorporate macroporous channels into a mesoporous TiO₂ framework to form mixed macro-mesoporous TiO₂ spheres (MMPT), which were doped with carbon dots (C-dots) to form improved nanocomposites (C-dots@MMPT). Elemental composition, surface bonding and optical properties of these nanocomposites were characterized by X-ray diffraction (XRD), Fourier transforms infrared spectroscopy (FTIR) and ultraviolet-visible absorption spectroscopy (UV-VIS). Evaluation of photocatalytic activity for each (C-Dots@MMPT) sample was performed via degrading the Methylene Blue (MB) dye compared with bare samples (MMPT) under visible light irradiation using 300 Watt halogen lamp.

In order to explore the influence of the ferroelectric surface on the structure and properties of semiconductor oxides, the growth of CdS nanocrystals was regulated and controlled by taking single-crystal perovskite PbTiO₃ nanosheets as the substrate through a simple hydrothermal method. Through composition design, a series of PbTiO₃-CdS nanocomposite materials with different loading concentrations were prepared, and their microstructure and photocatalytic properties were systematically analyzed. Studies show that in the prepared product, CdS nanoparticles selectively grow on the surfaces of PbTiO₃ nanosheets, and their morphology is affected by the exposed surfaces of PbTiO₃ nanosheets. There is a clear interface between the PbTiO₃ substrate and CdS nanoparticles. The concentration of the initial reactant and the time of hydrothermal reaction also significantly affect the crystal morphology of CdS. Photocatalysis studies have shown that the prepared PbTiO₃-CdS nanocomposite material has a significant degradation effect on 10 mg/L of Rhodamine B aqueous solution. The degradation efficiency rises with the increase of CdS loading concentration. When degrading 10 mg/L Rhodamine B aqueous solution, the PbTiO₃-CdS sample with a mass fraction of 3% can reach a degradation rate of 72% within 120 min.

Nowadays, copper and zinc nanoparticles are widely employed in a variety of applications. With nanoscale particle sizes, copper oxide/zinc oxide composite is easily synthesized using a variety of techniques, including hydrothermal, microwave, precipitation, etc. In the current work, chemical precipitation is used to create a copper oxide/zinc oxide nanocomposite. XRD analysis was used to determine the nanocomposite’s structural characteristics. Through SEM analysis, the surface morphological properties are investigated. EDAX is used to study the chemical composition of produced materials, while UV/Visible spectroscopy is used to determine their optical properties. The assessment of the copper oxide/zinc oxide nanocomposite’s degrading property on dyes like methyl red and methyl orange under UV and visible light are the main objectives of the current work.

ZnO nanostructures were obtained by electrodeposition on Ni foam, where graphene was previously grown by chemical vapor deposition (CVD). The resulting heterostructures were characterized by X-ray diffraction and SEM microscopy, and their potential application as a catalyst for the photodegradation of methylene blue (MB) was evaluated. The incorporation of graphene to the Ni substrate increases the amount of deposited ZnO at low potentials in comparison to bare Ni. SEM images show homogeneous growth of ZnO on Ni/G but not on bare Ni foam. A percent removal of almost 60% of MB was achieved by the Ni/G/ZnO sample, which represents a double quantity than the other catalysts proved in this work. The synergistic effects of ZnO-graphene heterojunctions play a key role in achieving better adsorption and photocatalytic performance. The results demonstrate the ease of depositing ZnO on seedless graphene by electrodeposition. The use of the film as a photocatalyst delivers interesting and competitive removal percentages for a potentially scalable degradation process enhanced by a non-toxic compound such as graphene.