Xylene isomers are notorious chemical hazards, and their efficient removal from water solutions is still challenging. The current study reports a polymer nanocomposite as a potential adsorbent for successfully removing dissolved xylene isomers from contaminated water. Polystyrene-1D multiwall carbon nanotube nanocomposite (PS-MWCNT) adsorbent was prepared using the one-step bulk polymerization method. Mesoporous PS-MWCNT was prepared using the nano-crystallization phase separation method. The sulfonation of the mesoporous PS-MWCNT nanocomposites was carried out by treating the samples with concentrated sulfuric acid at elevated temperatures. The sulfonated PS-MWCNT (HO₃S-PS-MWCNT) was found to be a potential adsorbent for dissolved xylene isomers from water solution. In addition, the HO₃S-PS-MWCNT can be efficiently recycled for up to 10 consecutive cycles with negligible decline in adsorption values. The exhibited equilibrium adsorption, rate of adsorption, and rapid regeneration of the HO₃S-PS-MWCNT are clear indications for the possibility of practical utilization of these adsorbents in large-scale water treatment plants.

The chemical reinforcement of sandy soils is usually carried out to improve their properties and meet specific engineering requirements. Nevertheless, conventional reinforcement agents are often expensive; the process is energy-intensive and causes serious environmental issues. Therefore, developing a cost-effective, room-temperature-based method that uses recyclable chemicals is necessary. In the current study, poly (styrene-co-methyl methacrylate) (PS-PMMA) is used as a stabilizer to reinforce sandy soil. The copolymer-reinforced sand samples were prepared using the one-step bulk polymerization method at room temperature. The mechanical strength of the copolymer-reinforced sand samples depends on the ratio of the PS-PMMA copolymer to the sand. The higher the copolymer-to-sand ratio, the higher the sample’s compressive strength. The sand (70 wt.%)-PS-PMMA (30 wt.%) sample exhibited the highest compressive strength of 1900 psi. The copolymer matrix enwraps the sand particles to form a stable structure with high compressive strengths.