This work investigates epoxy composites reinforced by randomly oriented, short glass fibres and silica microparticles. A full-factorial experiment evaluates the effects of glass fibre mass fraction (15 wt% and 20 wt%) and length (5 mm and 10 mm), and the mass fraction of silica microparticles (5 wt% and 10 wt%) on the apparent density and porosity, as well as the compressive and tensile strength and modulus of the hybrid composites. Hybrid epoxy composites present significantly higher tensile strength (9%) and modulus (57%), as well as compressive strength (up to 15%) relative to pure epoxy.

The objective of the present study is to observe the surface morphology, structure and elemental composition of the ash particles produced from some thermal power stations of India using scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDXA). This information is useful to better understand the ash particles before deciding its utility in varied areas.

The objective of this work was to evaluate the combined effect of bovine manure, Pseudomonas putida and Trichoderma aureoviride on the development of lettuce (Lactuca sativa). The promotion of plant growth by microorganisms may be a viable and sustainable alternative for lettuce crop management. The experimental design was entirely randomized with five treatments: T0 (witness without fertilization, P. putida and T. aureoviride), TE (cattle manure), TEB (cattle manure + P. putida), TEF (cattle manure + T. aureoviride), TEFB (cattle manure + P. putida + T. aureoviride) and ten repetitions each. The following variables were analyzed: germination velocity index (GVI), first count (FC), germination percentage (GP), leaf area index and productivity. The TEFB treatment proved to be a viable alternative for the production of lettuce, especially for small producers, since all the vegetable production in the region comes from family farming.

In this study, nano-scale microstructural evolution in 6061-T6 alloy after laser shock processing (LSP) was studied. 6061-T6 alloy plate was subjected to multiple LSP. The LSP treated area was characterized by X-ray diffraction and the microstructure of the samples was analyzed by transmission electron microscopy. Focused Ion Beam (FIB) tools were used to prepare TEM samples in precise areas. It was found that even though aluminum had high stacking fault energy, LSP yielded to formation of ultrafine grains and deformation faults such as dislocation cells, stacking faults. The stacking fault probability (PSF) was obtained in LSP-treated alloy using X-Ray diffraction. Deformation induced stacking faults lead to the peak position shifts, broadening and asymmetry of diffraction. XRD analysis and TEM observations revealed significant densities of stacking faults in LSP-treated 6061-T6 alloy. And mechanical properties of LSP-treated alloy were also determined to understand the hardening behavior with high concentration of structural defects.

This work is a part of research on the microstructure and mechanical properties of Cr-Ni-Si steels after various thermal treatments [1, 2]. The need to minimize damage and losses caused by emerging failures in complex engineering facilities such as nuclear, thermal and hydroelectric power stations, and gas and oil pipelines necessitates the creation of materials of high strength, plasticity, welding and high rigidity.