This work investigates epoxy composites reinforced by randomly oriented, short glass fibres and silica microparticles. A full-factorial experiment evaluates the effects of glass fibre mass fraction (15 wt% and 20 wt%) and length (5 mm and 10 mm), and the mass fraction of silica microparticles (5 wt% and 10 wt%) on the apparent density and porosity, as well as the compressive and tensile strength and modulus of the hybrid composites. Hybrid epoxy composites present significantly higher tensile strength (9%) and modulus (57%), as well as compressive strength (up to 15%) relative to pure epoxy.

The cross wire projection welding of wires (Al 5182, = 4 mm) performed using the conventional (i.e. pneumatic) electrode force system was subjected to thorough numerical analysis. Calculations were performed until one of adopted boundary conditions, i.e., maximum welding time, maximum penetration of wires, the occurrence of expulsion or the exceeding of the temperature limit in the contact between the electrode and the welded material was obtained. It was observed that the ring weld was formed within the entire range of welding parameters. The process of welding was subjected to optimisation through the application of a new electromechanical electrode force system and the use of a special hybrid algorithm of electrode force and/or displacement control. Comparative numerical calculations were performed (using SORPAS software) for both electrode force systems. Technological welding tests were performed using inverter welding machines (1 kHz) provided with various electrode force systems. The research also involved the performance of metallographic and strength (peeling) tests as well as measurements of welding process characteristic parameters (welding current and voltage).
The welding process optimisation involving the use of the electromechanical force system and the application of the hybrid algorithm of force control resulted in i) more favourable space distribution of welding power, ii) energy concentration in the central zone of the weld, iii) favourable (desired) melting of the material within the entire weld transcrystallisation zone and iv) obtainment of a full weld nugget.

Humic substances are used in agriculture as promoters of plant growth, especially of the root system. The objective of the work was to evaluate the effect of the application of different doses of fulvic acid on the growth and productivity of American lettuce, Raider Plus cultivar. The experimental design used was entirely randomized, with five treatments of fulvic acid 0, 1, 2, 4, 8 mL·L^-1 and four repetitions, applied at the time of transplanting. Two experiments were conducted simultaneously: one in the greenhouse, where fresh and dry mass of the aboveground and root parts, length and volume of the roots were evaluated; and the other in the field, where, at the end of the cycle, fresh and dry mass of the aboveground parts, number of leaves, stem length and average head circumference were evaluated. The application of different doses of fulvic acid promoted the growth of lettuce plants, especially the root system. The emission of roots, with predominance, of those of smaller diameter, was found in the higher concentrations of fulvic acid. The number of leaves and the average circumference of the head expressed responses in the concentrations of fulvic acid.