We develop a relatively cheap technology of processing a scrap in the form of already used tungsten-containing products (spirals, plates, wires, rods, etc.), as well not conditional tungsten powders. The main stages of the proposed W-scrap recycling method are its dispersing and subsequent dissolution under controlled conditions in hydrogen peroxide aqueous solution resulting in the PTA (PeroxpolyTungstic Acid) formation. The filtered solution, as well as the solid acid obtained by its evaporation, are used to synthesize various tungsten compounds and composites. Good solubility of PTA in water and some other solvents allows preparing homogeneous liquid charges, heat treatment of which yield WC and WC–Co in form of ultradispersed powders. GO (Graphene Oxide) and PTA composite is obtained and its phase transition in vacuum and reducing atmosphere (H₂) is studied. By vacuum-thermal exfoliation of GO–PTA composite at 170–500℃ the rGO (reduced GO) and WO_2.9 tungsten oxide are obtained, and at 700℃—rGO–WO₂ composite. WC, W₂C and WC–Co are obtained from PTA at high temperature (900–1000℃). By reducing PTA in a hydrogen atmosphere, metallic tungsten powder is obtained, which was used to obtain sandwich composites with boron carbide B₄C, W/B₄C, and W/(B₄C–W), as neutron shield materials. Composites of sandwich morphology are formed by SPS (Spark-Plasma Sintering) method.

Graphene has been ranked among one of the most remarkable nanostructures in the carbon world. Graphene modification and nanocomposite formation have been used to expand the practical potential of graphene nanostructure. The overview is an effort to highlight the indispensable synthesis strategies towards the formation of graphene nanocomposites. Consequently, graphene has been combined with useful matrices (thermoplastic, conducting, or others) to attain the desired end material. Common fabrication approaches like the in-situ method, solution processing, and melt extrusion have been widely involved to form the graphene nanocomposites. Moreover, advanced, sophisticated methods such as three- or four-dimensional printing, electrospinning, and others have been used to synthesize the graphene nanocomposites. The focus of all synthesis strategies has remained on the standardized graphene dispersion, physical properties, and applications. However, continuous future efforts are required to resolve the challenges in synthesis strategies and optimization of the parameters behind each technique. As the graphene nanocomposite design and properties directly depend upon the fabrication techniques used, there is an obvious need for the development of advanced methods having better control over process parameters. Here, the main challenging factors may involve the precise parameter control of the advanced techniques used for graphene nanocomposite manufacturing. Hence, there is not only a need for current and future research to resolve the field challenges related to material fabrication, but also reporting compiled review articles can be useful for interested field researchers towards challenge solving and future developments in graphene manufacturing.

Three-dimensionally cross-linked polymer nanocomposite networks coated nano sand light-weight proppants (LWPs) were successfully prepared via ball-milling the macro sand and subsequently modifying the resultant nano sand with sequential polymer nanocomposite coating. The modified nano sand proppants had good sphericity and roundness. Thermal analyses showed that the samples can withstand up to 411 ℃. Moreover, the proppant samples’ specific gravity (S.G.) was 1.02–1.10 g/cm³ with excellent water dispersibility. Therefore, cross-linked polymer nanocomposite networks coated nano sand particles can act as potential candidates as water-carrying proppants for hydraulic fracturing operations.

Graphene oxide can be referred to as oxidized graphene. Similar to graphene, oxidized graphene possesses remarkable structural features, advantageous properties, and technical applications. Among polymeric matrices, conducting polymers have been categorized for p conjugated backbone and semiconducting features. In this context, doping, or nano-additive inclusion, has been found to enhance the electrical conduction features of conjugated polymers. Like other carbon nanostructures (fullerene, carbon nanotube, etc.), graphene has been used to reinforce the conjugated matrices. Graphene can be further modified into several derived forms, including graphene oxide, reduced graphene oxide, and functionalized graphene. Among these, graphene oxide has been identified as an important graphene derivative and nanofiller for conducting matrices. This overview covers essential aspects and progressions in the sector of conjugated polymers and graphene oxide derived nanomaterials. Since the importance of graphene oxide derived nanocomposites, this overview has been developed aiming at conductive polymer/graphene oxide nanocomposites. The novelty of this article relies on the originality and design of the outline, the review framework, and recent literature gathering compared with previous literature reviews. To the best of our knowledge, such an all-inclusive overview of conducting polymer/graphene oxide focusing on fundamentals and essential technical developments has not been seen in the literature before. Due to advantageous structural, morphological, conducting, and other specific properties, conductive polymer/graphene oxide nanomaterials have been applied for a range of technical applications such as supercapacitors, photovoltaics, corrosion resistance, etc. Future research on these high-performance nanocomposites may overcome the design and performance-related challenges facing industrial utilization.

The application of nanotechnology in the food industry enables prioritization of consumers’ needs. Nanotechnology has the ability to provide new forms of control on food structure; therefore, this technology has higher industrial value. This paper briefly introduces the main concepts of nanotechnology and its correlation with size reduction performance. This paper also introduces the main nanobjects and their potential applications in food, and summarizes various studies and their applications in food industry.

Diamond-like Nanocomposites (DLN) is a newly member in amorphous carbon (a:C) family. It consists of two or more interpenetrated atomic scale network structures. The amorphous silicon oxide (a:SiO) is incorporated within diamond-like carbon (DLC) matrix i.e. a:CH and both the network is interpenetrated by Si-C bond. Hence, the internal stress of deposited DLN film decreases remarkably compare to DLC. The diamond-like properties have come due to deform tetrahedral carbon with sp³ configuration and high ratio of sp³ to sp² bond. The DLN has excellent mechanical, electrical, optical and tribological properties. Those properties of DLN could be varied over a wide range by changing deposition parameters, precursor and even post deposition treatment also. The range of properties are: Resistivity 10^-4 to 10¹⁴ Ωcm, hardness 10–22 GPa, coefficient of friction 0.03-0.2, wear factor 0.2-0.4 10^-7mm³/Nm, transmission Vis-far IR, modulus of elasticity 150-200 GPa, residual stress 200-300 Mpa, dielectric constant 3-9 and maximum operating temperature 600^°C in oxygen environment and 1200^°C in O₂ free air. Generally, the PECVD method is used to synthesize the DLN film. The most common procedures used for investigation of structure and composition of DLN films are Raman spectroscopy, Fourier transformed infrared spectroscopy (FTIR), HRTEM, FESEM and X-ray photo electron spectroscopy (XPS). Interest in the coating technology has been expressed by nearly every industrial segment including automotive, aerospace, chemical processing, marine, energy, personal care, office equipment, electronics, biomedical and tool and die or in a single line from data to beer in all segment of life. In this review paper, characterization of diamond-like nanocomposites is discussed and subsequently different application areas are also elaborated.