Gold nanoparticles (AuNPs) have been known to possess exceptional electric, biochemical, and optical characteristics and are ‘the topic of discussion’ these days, especially relating to the field of biomedicine. Several plants, bacteria, and fungi have been utilized for the generation of AuNPs, besides other physical and chemical methods. While some studies have been reported with gold nanoparticles, less are aimed at fungi and its optimization factors. These parameters can allow us to design AuNPs of our choice depending on the use. The present review focuses on and inspects AuNPs with green synthesis through fungus optimization parameters followed by applications, aiming specifically at their antibacterial activity. Their antibacterial characteristics can open new doors for the pharmaceutical industry in the future.

Zero-valent iron is a moderately reducing reagent that is both non-toxic and affordable. In the present work, iron nanoparticles were synthesized using bitter guard leaf extract (Momordica charantia L.) (BGL-Fe NP). Using leaf samples from bitter protectant extract, iron nanoparticles were synthesized with secondary metabolites such as flavonoids and polyphenols acting as capping and reducing agents. Polyphenols reduce Fe²⁺/Fe³⁺ to nanovalent iron or iron nanoparticles. Iron nanoparticles were synthesized by reducing iron chloride as a precursor with bitter protective leaf extract in an alkaline environment. The obtained BGL-Fe NPs were calcined for 4 h at various temperatures of 400 °C, 500 °C, and 600 °C. The obtained samples were coded as BGL-Fe NPs-4, BGL-Fe NPs-5, and BGL-Fe NPs-6, respectively. The synthesized BGL-Fe NPs were systematically characterized by XRD, SEM, FTIR, UV-Vis and TG-DTA analysis. The obtained BGL-Fe NPs were then used as an adsorbent to remove the aqueous solution of basic methylene blue (MB) dye. MB concentration was monitored using UV-Vis spectroscopy.

This work presents the evaluation of iron oxide nanoparticles obtained from the aqueous extract of Eucalyptus grandis. Twenty-three experiments were carried out where the synthesis of nanoparticles was performed by using the aqueous extract together with salts of iron (II) chloride tetrahydrate and iron (III) chloride hexahydrate. A characterization was carried out by IR, TEM and BET, where bands were presented at 3,440.77, 1,559.26 and 445.31 cm⁻¹, indicating the presence of iron oxide nanoparticles. A relatively high monodispersity was evidenced with particles around 9 nm. By means of BET analysis it was found to present a surface area of 131.897 m²/g. Obtaining nanoparticles by this green method presents yield values of 98%, with application in nanotechnology, biomedicine, environmental treatment, among others, making them highly versatile and their production cost is relatively low.