Three-dimensionally cross-linked polymer nanocomposite networks coated nano sand light-weight proppants (LWPs) were successfully prepared via ball-milling the macro sand and subsequently modifying the resultant nano sand with sequential polymer nanocomposite coating. The modified nano sand proppants had good sphericity and roundness. Thermal analyses showed that the samples can withstand up to 411 ℃. Moreover, the proppant samples’ specific gravity (S.G.) was 1.02–1.10 g/cm³ with excellent water dispersibility. Therefore, cross-linked polymer nanocomposite networks coated nano sand particles can act as potential candidates as water-carrying proppants for hydraulic fracturing operations.

Graphene oxide can be referred to as oxidized graphene. Similar to graphene, oxidized graphene possesses remarkable structural features, advantageous properties, and technical applications. Among polymeric matrices, conducting polymers have been categorized for p conjugated backbone and semiconducting features. In this context, doping, or nano-additive inclusion, has been found to enhance the electrical conduction features of conjugated polymers. Like other carbon nanostructures (fullerene, carbon nanotube, etc.), graphene has been used to reinforce the conjugated matrices. Graphene can be further modified into several derived forms, including graphene oxide, reduced graphene oxide, and functionalized graphene. Among these, graphene oxide has been identified as an important graphene derivative and nanofiller for conducting matrices. This overview covers essential aspects and progressions in the sector of conjugated polymers and graphene oxide derived nanomaterials. Since the importance of graphene oxide derived nanocomposites, this overview has been developed aiming at conductive polymer/graphene oxide nanocomposites. The novelty of this article relies on the originality and design of the outline, the review framework, and recent literature gathering compared with previous literature reviews. To the best of our knowledge, such an all-inclusive overview of conducting polymer/graphene oxide focusing on fundamentals and essential technical developments has not been seen in the literature before. Due to advantageous structural, morphological, conducting, and other specific properties, conductive polymer/graphene oxide nanomaterials have been applied for a range of technical applications such as supercapacitors, photovoltaics, corrosion resistance, etc. Future research on these high-performance nanocomposites may overcome the design and performance-related challenges facing industrial utilization.

The application of nanotechnology in the food industry enables prioritization of consumers’ needs. Nanotechnology has the ability to provide new forms of control on food structure; therefore, this technology has higher industrial value. This paper briefly introduces the main concepts of nanotechnology and its correlation with size reduction performance. This paper also introduces the main nanobjects and their potential applications in food, and summarizes various studies and their applications in food industry.

Diamond-like Nanocomposites (DLN) is a newly member in amorphous carbon (a:C) family. It consists of two or more interpenetrated atomic scale network structures. The amorphous silicon oxide (a:SiO) is incorporated within diamond-like carbon (DLC) matrix i.e. a:CH and both the network is interpenetrated by Si-C bond. Hence, the internal stress of deposited DLN film decreases remarkably compare to DLC. The diamond-like properties have come due to deform tetrahedral carbon with sp³ configuration and high ratio of sp³ to sp² bond. The DLN has excellent mechanical, electrical, optical and tribological properties. Those properties of DLN could be varied over a wide range by changing deposition parameters, precursor and even post deposition treatment also. The range of properties are: Resistivity 10^-4 to 10¹⁴ Ωcm, hardness 10–22 GPa, coefficient of friction 0.03-0.2, wear factor 0.2-0.4 10^-7mm³/Nm, transmission Vis-far IR, modulus of elasticity 150-200 GPa, residual stress 200-300 Mpa, dielectric constant 3-9 and maximum operating temperature 600^°C in oxygen environment and 1200^°C in O₂ free air. Generally, the PECVD method is used to synthesize the DLN film. The most common procedures used for investigation of structure and composition of DLN films are Raman spectroscopy, Fourier transformed infrared spectroscopy (FTIR), HRTEM, FESEM and X-ray photo electron spectroscopy (XPS). Interest in the coating technology has been expressed by nearly every industrial segment including automotive, aerospace, chemical processing, marine, energy, personal care, office equipment, electronics, biomedical and tool and die or in a single line from data to beer in all segment of life. In this review paper, characterization of diamond-like nanocomposites is discussed and subsequently different application areas are also elaborated.

Among carbon nanoparticles, fullerene has been observed as a unique zero-dimensional hollow molecule. Fullerene has a high surface area and exceptional structural and physical features (optical, electronic, heat, mechanical, and others). Advancements in fullerene have been observed in the form of nanocomposites. Application of fullerene nanocomposites has been found in the membrane sector. This cutting-edge review article basically describes the potential of fullerene nanocomposite membranes for water remediation. Adding fullerene nanoparticles has been found to amend the microstructure and physical features of the nanocomposite membranes in addition to membrane porosity, selectivity, permeation, water flux, desalination, and other significant properties for water remediation. Variations in the designs of fullerene nanocomposites have resulted in greater separations between salts, desired metals, toxic metal ions, microorganisms, etc. Future investigations on ground-breaking fullerene-based membrane materials may overcome several design and performance challenges for advanced applications.

Industrial plastics have seen considerable progress recently, particularly in manufacturing non-lethal projectile holders for shock absorption. In this work, a variety of percentages of alumina (Al₂O₃) and carbon black (CB) were incorporated into high-density polyethylene (HDPE) to investigate the additive material effect on the consistency of HDPE projectile holders. The final product with the desired properties was controlled via physical, thermal, and mechanical analysis. Our research focuses on nanocomposites with a semicrystalline HDPE matrix strengthened among various nanocomposites. In the presence of compatibility, mixtures of variable compositions from 0 to 3% by weight were prepared. The reinforcement used was verified by X-ray diffraction (XRD) characterization, and thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) were used for thermal property investigation. Alumina particles increased the composites’ thermal system and glass transition temperature. Mechanical experiments indicate that incorporating alumina into the matrix diminishes impact resistance while augmenting static rupture stress. Scanning electron microscopy (SEM) revealed a consistent load distribution. Ultimately, we will conduct a statistical analysis to compare the experimental outcomes and translate them into mathematical answers that elucidate the impact of filler materials on the HDPE matrix.