In order to replace conventional materials in the existing composite world, there has been a focus on adopting coir fibres, which are lightweight, adaptable, efficient, and have great mechanical qualities. This study describes the creation of environmentally responsible bio-composites with good mechanical characteristics that employ coir powder as a reinforcement, which has good interfacial integrity with an epoxy matrix. And these epoxy-coir composites supplemented with coir particles are predicted to function as a reliable substitute for traditional materials used in industrial applications. Here, untreated and alkali-treated coir fibres powder were employed as reinforcement, with epoxy resin serving as a matrix. An experimental investigation has been carried out to study the effect of coir powder reinforcement at different weight percentages (5 wt%, 10 wt%, 15 wt%, 20 wt%, 25 wt%, and 30 wt%). The morphological study, followed by a scanning electron microscope (SEM) and an optical microscope (OM), demonstrated that the powder and matrix had the strongest adhesion at 20 wt% coir powder-reinforced composite, with no voids, bubbles, or cracks. Based on the entire investigation, the polymer composite with 20 wt% reinforcement exhibited better mechanical qualities than the other combinations.

In response to the challenges of climate change, this study explores the use of moringa pod powder as reinforcement in the manufacture of compressed earth bricks to promote sustainable building materials. The objective is to evaluate the impact of African locust bean pod powder on the mechanical properties of the bricks. Two types of soils from Togo were characterized according to geotechnical standards. Mixtures containing 8% African locust bean pod powder at various particle sizes (0.08 mm, 2 mm, and between 2 and 5 mm) were formulated and tested for compression and tensile strength. The results show that the addition of African locust bean pod reduces the mechanical strength of the bricks compared to the control sample without pods, with strengths ranging from 0.697 to 0.767 MPa, compared to 0.967 to 1.060 MPa for the control. However, the best performances for the mixtures were obtained with a fineness of less than 2 mm. This decrease in performance is attributed to several factors, including inadequate water content and suboptimal preparation and compaction methods. Optimizing formulation parameters is necessary to maximize the effectiveness of African locust bean pods. This work highlights the valorization of agro-industrial waste, paving the way for a better understanding of bio-based materials and future research for sustainable construction.