Ce⁴⁺-doped nanometer ZnO powder was synthesized by so-l gel method. The microstructures and properties of the samples were characterized through XRD, UV-Vis and FTIR. The results indicated that the Ce⁴⁺ was successfully incorporated into ZnO, and the diameter of the nanometer was about 10.7nm. It induced the redshifting in the UV-Vis spectra. The photocatalytic activity of the samples was investigated using methylene blue (MB) as the model reaction under irradiation with ultraviolet light. The results showed that the doping of Ce⁴⁺ could increase the photocatalytic activities of ZnO nanopowders and that the best molar ratio of Ce⁴⁺ was n(Ce)/n(Zn) = 0.05, that the surfactant was sodium dodecyl sulfate, and that the nanometer ZnO was calcinated at 550 ℃ for 3 hours. Meanwhile, it inspected the effect of photocatalytic efficiency through the pH of MB, the amount of catalyst, and illumination time. The experimental results revealed that the initial mass concentration of MB was 10 mg/L, that the pH value was 7-8, that the dosage of Ce⁴⁺/ZnO photo-catalyst was 5 g/L, that the UV-irradiation time was 2 h, and that the removal rate of MB reached above 85%. Under the optimized conditions, the degradation rate of real dye wastewater was up to 87.67% and the removal efficiency of COD was 63.5%.

It has become commonplace to describe publicly provided infrastructure as being in a sorry state and to advance public-private partnership as a possible remedy. This essay adopts a skeptical but not a cynical posture toward those claims. The paper starts by reviewing the comparative properties of markets and politics within a theory of budgeting where the options are construction and maintenance. This analytical point of departure explains how incongruities between political and market action can favor construction over maintenance. In short, political entities can engage in an implicit form of public debt by reducing maintenance spending to support other budgetary items. This implicit form of public debt does not manifest in higher interest rates but rather manifests in crumbling bridges and other infrastructure due to the transfer of maintenance into other budgetary activities.

This study analyzes the influence of five primary factors—inflation, capital ratio, deposits, non-performing loans, and bank size—on the performance of banks in Vietnam. Our sample encompasses 26 commercial banks from 2014 to 2023. The analysis incorporates data sourced from commercial banks’ financial statements and annual reports. Our findings indicate that banks with higher capital ratios and sizes generally exhibit superior performance. Moreover, inflation positively influences the performance of Vietnamese commercial banks throughout the selected timeframe. In contrast, non-performing loans and deposits are inverse to bank performance. Our findings offer novel insights into the factors influencing bank performance in a growing economy like Vietnam, along with recommendations for Vietnamese commercial banks and the State Bank of Vietnam to implement effective methods to improve bank performance.