Water splitting has been one of the potential techniques as a clean and renewable energy resource for the fulfillment of world energy demands. One of the major aspects of this procedure is the exploitation of efficient and inexpensive electrocatalysts due to the fact that the water oxidation procedure is accompanied by a delayed reaction. In this research, ZnO-CoFe₂O₄ nanostructure was successfully synthesized via the green method and green resources from cardamom seeds and ginger peels for oxygen evolution reaction (OER). The modified Glassy carbon electrode (GCE) with ZnO-CoFe₂O₄ is effective for the electrochemical water oxidation interaction since it has sufficient electrical strength and excellent catalytic performance. The creation of rice-like and small granular structures of ZnO-CoFe₂O₄ nano-catalysts was confirmed by characterization methods such as XRD, FESEM, EDS and MAP. According to the achieved results, in the electrolysis of water, with in-cell voltage of 1.40 V and 50 mA cm^–2 for current density in a 0.1 M KOH electrolyte and OER only has 170 mV overpotentials.

Zero-valent iron is a moderately reducing reagent that is both non-toxic and affordable. In the present work, iron nanoparticles were synthesized using bitter guard leaf extract (Momordica charantia L.) (BGL-Fe NP). Using leaf samples from bitter protectant extract, iron nanoparticles were synthesized with secondary metabolites such as flavonoids and polyphenols acting as capping and reducing agents. Polyphenols reduce Fe²⁺/Fe³⁺ to nanovalent iron or iron nanoparticles. Iron nanoparticles were synthesized by reducing iron chloride as a precursor with bitter protective leaf extract in an alkaline environment. The obtained BGL-Fe NPs were calcined for 4 h at various temperatures of 400 °C, 500 °C, and 600 °C. The obtained samples were coded as BGL-Fe NPs-4, BGL-Fe NPs-5, and BGL-Fe NPs-6, respectively. The synthesized BGL-Fe NPs were systematically characterized by XRD, SEM, FTIR, UV-Vis and TG-DTA analysis. The obtained BGL-Fe NPs were then used as an adsorbent to remove the aqueous solution of basic methylene blue (MB) dye. MB concentration was monitored using UV-Vis spectroscopy.

Broad-spectrum antibiotics, such as tetracyclines, are used to treat and manage a range of infectious disorders. Since the kidneys are the primary organs responsible for excreting tetracyclines, clinicians should refrain from prescribing them to patients who have renal failure. Tetracyclines are one of the clinical waste products of today. One of the biggest problems in the field of pollution of the environment today is the persistence of different pharmaceutical residues, drug residues, pesticides, and metal ion species of the new-generation pollutants in surfaces and groundwater. In the present work, carboxymethyl cellulose (CMC)-CuO nanoparticles (CMC-CuO NPs) were synthesized using CuO NPs within different amounts of CMC (0.5, 1.0, 1.5 and 2.0 g) at 85 °C. The synthesized nanoparticles were characterized by XRD, FT IR, SEM, and TG-DTA analysis. According to XRD and SEM, the crystallize size and morphology influenced the dosage of CMC. FT-IR analysis confines the layer of CMC to the CuO nanoparticle surface. TG-DTA results indicated that the CMC content of CMC-CuO NPs was between the range of 69% and 75% by weight. The effects of some parameters such as initial concentration, pH, adsorbent dosage, and contact time on the adsorption of tetracycline from aqueous model solutions on CMC-CuO NPs were investigated with batch studies. It was found that the removal of tetracycline was obtained about 80% with optimized parameters of 10 mg/L concentration, 180 min contact time, 5 pH, and 0.3 g/25 mL dose. The synthesized CMC-CuO NPs nanocomposite may be a promising material for the removal of tetracycline in environmental pollution and toxicology.

Beta macrocarpa, Guss is an interesting species showing very low germination rates. The leading objectives of this work were to investigate the dormancy mechanism and to find methods to break dormancy in order to achieve rapid, uniform and high germination. Macro and micro-morphologic analyses were performed by stereo microscopy and scanning electron microscopy showed two fruit coats. The yellow external coat or persistent perianth coat (PPC) was accrescent with 5 erect segments contiguous to the operculum of the seed capsule. This coat forms spongy layers (50 to 300 µm thick) that could be eliminated manually. The narrow internal coat or pericarp or achene coat (AC) forms woody joined seed capsules, each presenting a pressed operculum that cannot be manually opened. This coat was not adherent to seeds and was composed of compressed cells (50 to 200 µm thick) which form pockets for salt cristal. Seeds were lentiform (1 to 2 mm diameter and 0.5 to 0.8 mm thick) and highly fragile. The embryo was whitish surrounded peripherally by the perisperm with two highly developed cotyledons and radical. Polyphenol concentrations in both coats showed that after 4 months of collection, total polyphenol concentrations were 4-fold higher in the pericarp than in the persistent perianth. However, after one year, this parameter decreases significantly in the pericarp, whereas, it increases to a larger extent in the perianth. Different germination tests indicated that the pericarp provides a chemical and a physical resistance to seed germination during the first 4 months of the experiment after collection. The chemical dormancy was released to higher levels of total polyphenol compounds that inhibited seed germination and seedling growth. However, the physical dormancy was associated with the hardness of this intern coat which caused a mechanical resistance to radicle emergence. After one year of storage, total polyphenol pericarp concentration decreased notably, and chemical resistance disappeared, whereas the physical one persisted. Consequently, one year of storage pericarp removal is sufficient to break this exogenous dormancy.

City planning is becoming more and more crucial as modernization and urbanization progress quickly. Making maps is an essential and helpful way in the city planning process for gathering data about the layout of a city and its elements, including the roads, traffic, buildings, and environment. Thanks to advancements in technology, computer software is now used to create maps, yielding more accurate and varied results. As a result, cartography is now closely related to and plays a crucial part in city planning. This brief essay will discuss the value of cartography in urban development and planning, as well as the connection between the two.