Surface-enhanced Raman scattering (SERS) spectrum has the characteristics of fast-detection, high-sensitivity and low-requirements for sample pretreatment. It plays a more and more important role in the detection of organic pollutants. In this study, MIL-101 and Au nanoparticles were prepared by hydrothermal method and aqueous solution reduction method respectively, and MIL-101/Au composite nanoparticles were prepared by electrostatic interaction. The SERS properties of the composite substrate were optimized by adjusting the size of Au nanoparticles and the surface distribution density of MIL-101 nanoparticles. The detection limit of Rhodamine 6G (R6G) for the composite substrate with the optimal ratio was investigated, which was as low as 10^–11 M. It is proved that MIL-101/Au composite nanoparticles have high sensitivity to probe molecules. When they are applied to the detection of persistent organic pollutants, the detection limit for fluoranthene can reach 10^–9 M and for 3,3’,4,4’-tetrachlorobiphenyl (PCB-77) can reach 10^–5 M.

In this paper, a classification of low-dimensional nanomaterials is given, and new type of these nanomaterials — subnanophase coatings are proposed. Experimental results on the formation of a wetting layer of a transition metal on a silicon substrate by physical deposition in vacuum and results of this layer identification by the EELS method are given. Based on these results, a new approach to the formation of subnanophase coatings has been proposed by creation of an interface stresses structuring WL. The possible properties and application prospects of subnanophase coatings are considered.

Attempts were made in the present study to design and develop skeletally modified ether linked tetraglycidyl epoxy resin (TGBAPSB), which is subsequently reinforced with different weight percentages of amine functionalized mullite fiber (F-MF). The F-MF was synthesized by reacting mullite fiber with 3-aminopropyltriethoxysilane (APTES) as coupling agent and the F-MF structure was confirmed by FT-IR. TGBAPSB reinforced with F-MF formulation was cured with 4,4’-diamino diphenyl methane (DDM) to obtain nanocomposite. The surface morphology of TGBAPSB-F-MF epoxy nanocomposites was investigated by XRD, SEM and AFM studies. From the study, it follows that these nanocomposite materials offer enhancement in mechanical, thermal, thermo-mechanical, dielectric properties compared to neat (TGBAPSB) epoxy matrix. Hence we recommend these nanocomposites for a possible use in advanced engineering applications that require both toughness and stiffness.

This research study explores the addition of chromium (Cr⁶⁺) ions as a nucleating agent in the alumino-silicate-glass (ASG) system (i.e., Al₂O₃-SiO₂-MgO-B₂O₃-K₂O-F). The important feature of this study is the induction of nucleation/crystallization in the base glass matrix on addition of Cr⁶⁺ content under annealing heat treatment (600 ± 10 °C) only. The melt-quenched glass is found to be amorphous, which in the presence of Cr⁶⁺ ions became crystalline with a predominant crystalline phase, Spinel (MgCr₂O₄). Microstructural experiment revealed the development of 200–500 nm crystallite particles in Cr⁶⁺-doped glass-ceramic matrix, and such type microstructure governed the mechanical properties. The machinability of the Cr-doped glass-ceramic was thereby higher compared to base alumino-silicate glass (ASG). From the nano-indentation experiment, the Young’s modulus was estimated 25(±10) GPa for base glass and increased to 894(±21) GPa for Cr-doped glass ceramics. Similarly, the microhardness for the base glass was 0.6(±0.5) GPa (nano-indentation measurements) and 3.63(±0.18) GPa (micro-indentation measurements). And that found increased to 8.4(±2.3) (nano-indentation measurements) and 3.94(±0.20) GPa (micro-indentation measurements) for Cr-containing glass ceramic.

With the progress of science and technology, the research and development of silver nanoparticles has also developed. This paper attempts to prepare a silver nanoparticle by electrolyzing AgNO3 solution with electrochemical reduction method and citric acid as a complexing agent in a certain current and time. The crystal morphology and sample purity of silver nanoparticles were analyzed by X-ray diffractometer. The crystal structure of the nanoparticles was analyzed by scanning electron microscopy (SEM). The crystal structure of the nanoparticles was analyzed by X-ray diffraction. The particle size distribution of the particles was in the range of 125-199 nm, and the carbon paste electrode was modified with the prepared silver nanoparticles. The electrocatalytic activity of the carbon paste electrode was preliminarily explored.

Nickel Oxide (NiO) nanoparticles (NPs), doped with manganese (Mn) and cobalt (Co) at concentrations up to 8%, were synthesized using the composite hydroxide method (CHM). X-ray diffraction (XRD) analysis confirmed the formation of a cubic NiO structure, with no additional peaks detected, indicating successful doping. The average crystallite size was determined to range from 15 to 17.8 nm, depending on the dopant concentration. Scanning electron microscopy (SEM) images revealed mostly spherical, agglomerated particles, likely due to magnetic interactions. Fourier Transform Infrared Spectroscopy (FTIR) confirmed the incorporation of Mn and Co into the NiO lattice, consistent with the XRD results. The dielectric properties exhibited a high dielectric constant at low frequencies, which can be attributed to ion jump orientation and space charge effects. The imaginary part of the dielectric constant decreased with increasing frequency, as it became harder for electrons to align with the alternating field at higher frequencies. Both the real and imaginary dielectric constants showed behavior consistent with Koop’s theory, increasing at low frequencies and decreasing at higher frequencies. Dielectric loss was primarily attributed to dipole flipping and charge migration. AC conductivity increased with frequency, and exhibited higher conductivity at high frequencies due to small polaron hopping. These co-doped NPs show potential for applications in solid oxide fuel cells.