This work presents the evaluation of iron oxide nanoparticles obtained from the aqueous extract of Eucalyptus grandis. Twenty-three experiments were carried out where the synthesis of nanoparticles was performed by using the aqueous extract together with salts of iron (II) chloride tetrahydrate and iron (III) chloride hexahydrate. A characterization was carried out by IR, TEM and BET, where bands were presented at 3,440.77, 1,559.26 and 445.31 cm⁻¹, indicating the presence of iron oxide nanoparticles. A relatively high monodispersity was evidenced with particles around 9 nm. By means of BET analysis it was found to present a surface area of 131.897 m²/g. Obtaining nanoparticles by this green method presents yield values of 98%, with application in nanotechnology, biomedicine, environmental treatment, among others, making them highly versatile and their production cost is relatively low.

Heat removal has become an increasingly crucial issue for microelectronic chips due to increasingly high speed and high performance. One solution is to increase the thermal conductivity of the corresponding dielectrics. However, traditional approach to adding solid heat conductive nanoparticles to polymer dielectrics led to a significant weight increase. Here we propose a dielectric polymer filled with heat conductive hollow nanoparticles to mitigate the weight gain. Our mesoscale simulation of heat conduction through this dielectric polymer composite microstructure using the phase-field spectral iterative perturbation method demonstrates the simultaneous achievement of enhanced effective thermal conductivity and the low density. It is shown that additional heat conductivity enhancement can be achieved by wrapping the hollow nanoparticles with graphene layers. The underlying mesoscale mechanism of such a microstructure design and the quantitative effect of interfacial thermal resistance will be discussed. This work is expected to stimulate future efforts to develop light-weight thermal conductive polymer nanocomposites.

Branched micro/nano Se was prepared by the redaction of L-Cys•HCl and H₂SeO₃ in hydrothermal method, as β-CD was used as soft template. The structures of products were characterized by SEM, TEM and XRD. Some important factors influencing the morphology of products were studied and discussed, including the amounts of soft template, the reaction temperature and the reaction time. The results showed that external causes had a potent effect on the morphology of micro/nano Se. The uniform branched micro/nano Se prepared under the optimal reaction condition was rhombohedral trigonal selenium t-Se⁰, but its crystallinity degree was low.