In order to explore the influence of the ferroelectric surface on the structure and properties of semiconductor oxides, the growth of CdS nanocrystals was regulated and controlled by taking single-crystal perovskite PbTiO₃ nanosheets as the substrate through a simple hydrothermal method. Through composition design, a series of PbTiO₃-CdS nanocomposite materials with different loading concentrations were prepared, and their microstructure and photocatalytic properties were systematically analyzed. Studies show that in the prepared product, CdS nanoparticles selectively grow on the surfaces of PbTiO₃ nanosheets, and their morphology is affected by the exposed surfaces of PbTiO₃ nanosheets. There is a clear interface between the PbTiO₃ substrate and CdS nanoparticles. The concentration of the initial reactant and the time of hydrothermal reaction also significantly affect the crystal morphology of CdS. Photocatalysis studies have shown that the prepared PbTiO₃-CdS nanocomposite material has a significant degradation effect on 10 mg/L of Rhodamine B aqueous solution. The degradation efficiency rises with the increase of CdS loading concentration. When degrading 10 mg/L Rhodamine B aqueous solution, the PbTiO₃-CdS sample with a mass fraction of 3% can reach a degradation rate of 72% within 120 min.

The Cu_2–xSe nanoparticles were synthesized by high temperature pyrolysis, modified with aminated polyethylene glycol in aqueous solution and loaded with compound 2,2′–azobis[2–(2–imidazolin–2–yl)propane] dihydrochloride (AIPH). The obtained nanomaterials can induce photothermal effect and use heat to promote the generation of toxic AIPH radicals under the irradiation of near-infrared laser (808 nm), which can effectively kill cancer cells. A series of in vitro experiments can preliminarily prove that Cu_2–xSe–AIPH nanomaterials have strong photothermal conversion ability, good biocompatibility and anticancer properties.

In this paper, spherical gold nanoparticles (AuNPs), rod-shape AuNPs and triangular AuNPs were synthesized using CTAB as the coating reagent, and their bactericidal properties against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) were studied. By the plate count method and turbidity method, the minimum bactericidal concentrations (MBC) and the minimum bacteriostasis concentrations (MIC) to the two kinds of bacteria were determined. The MIC of rod-shape AuNPs, triangular AuNPs and spherical AuNPs to E. coli were 0.65 μg/mL, 3.71 μg/mL, 21.21 μg/mL, and MBC were 1.30 μg/mL, 11.09 μg/mL, 21.21 μg/mL, respectively. The MIC to S. aureus were 0.26 μg/mL, 0.56 μg/mL, 2.65 μg/mL, while MBC were 0.52 μg/mL, 1.11 μg/mL, 2.65 μg/mL, respectively. The results showed that the bactericidal effect of rod-shape AuNPs on E. coli and S. aureus was higher than that of the other two forms, and the bactericidal effect of three different forms of AuNPs on S. aureus was better than that on E. coli.