The Cu_2–xSe nanoparticles were synthesized by high temperature pyrolysis, modified with aminated polyethylene glycol in aqueous solution and loaded with compound 2,2′–azobis[2–(2–imidazolin–2–yl)propane] dihydrochloride (AIPH). The obtained nanomaterials can induce photothermal effect and use heat to promote the generation of toxic AIPH radicals under the irradiation of near-infrared laser (808 nm), which can effectively kill cancer cells. A series of in vitro experiments can preliminarily prove that Cu_2–xSe–AIPH nanomaterials have strong photothermal conversion ability, good biocompatibility and anticancer properties.

An α, α^′-dipyridyl adduct of a complex compound hexaaquatribenzene-1,2,4,5-tetracarbonatotetra iron (III) with porous structure was synthesized for the first time. According to the results of elemental, X-ray, IR-spectroscopic and differential-thermal analyses the individuality, chemical formula, thermal destruction, and form of coordination of acidic anion and dipyridyl were established. During interaction of a complex compound with dipyridyl, it completely loses all crystallization molecule of water resulting in a compound with a chemical formula of Fe₄(C₆H₂(COO)₄)₃(dpy)₂(dipyridyl). Using the identification of diffraction pattern the parameters of lattice cell of the complex compound were determined.

In this paper, electrically conductive composites comprised of silicone rubber and titanium diboride (TiB₂) were synthesized by conventional mixing methods. Fine particles of TiB₂ (in micron size) and 10 parts per hundred parts of rubber (phr) proportion of carbon black (XC-72) were used to make the composites with HTV silicone rubber. The composites were cured at appropriate temperature and pressure and the effect on the electrical properties was studied. The resistance of the silicone rubber is ~ 10¹⁵Ω which decreases to 1–2 kΩ in case of composites with negligible effect of heat ageing. The hardness increases by ~ 35% simultaneous to the decrease of ~ 47% in the tensile strength. Morphological characterization indicates the homogeneous dispersion of the fillers in the composite.

Prepolymers containing isocyanates must be prevented from curing when exposed to moisture, which can be achieved by blocking the isocyanate groups with a suitable agent. The study carefully examines several blocking agents, including methyl ethyl ketoxime (MEKO), caprolactam, and phenol, and concludes that methyl ethyl ketoxime is the best choice. Spectroscopic and thermal analyses, as well as oven curing studies, are conducted with various blocking agents and isocyanate prepolymer to castor oil ratios, revealing MEKO to be the most effective blocking agent which gets unblocked at higher temperatures.

Magnesium hydroxide/melamine phosphate borate (nano MH/MPB), a novel nano-composition intumescent flame retardant, was synthesized with the in-situ reaction method from MgCl₂·6H₂O sodium hydroxide (NaOH) and melamine phosphate borate (MPB) in the absence of H₂O. The structure of the product was confirmed by EDAX IR and XRD. The effects of reaction temperature and time on the dimension of magnesium hydroxide were observed. The effects of mass ratio of magnesium hydroxide to MPB on the flame retardancy of nano-MH/MPB/EP were examined with the limiting oxygen test. The results show that the optimal condition of synthesis of MH/MPB is m_MH/m_MPB = 0.25, reacting under 75 ℃ for 30 minutes. Finally, the mechanism for flame retardancy of nano-MH/MPB/EP was pilot studied by means of IR of char layer and TG of MH/MPB.

The porous carbon/Ni nanoparticle composite was prepared by a freeze-drying method using NaCl as the template. It was applied in the effect of the concentration, adsorption time, and temperature of adsorption on the adsorption behavior. The kinetic model and the adsorption isothermic fitting results show that the adsorption behavior fits with the pseudo-secondary dynamics and the Langmuir isothermal model, indicating that the adsorption process is monolayer adsorption. Thermodynamic results indicate that the adsorption process is spontaneous physicochemical adsorption. The fitting showed that the porous carbon/Ni nanoparticle composites reach 217.17 mg·g^-1, at 313 K indicates good adsorption for Congo red.