Herein, we report a facile preparation of super-hydrophilic sand by coating the sand particles with cross-linked polyacrylamide (PAM) hydrogels for enhanced water absorption and controlled water release aimed at desert agriculture. To prepare the sample, 4 wt% of aqueous PAM solution is mixed with organic cross-linkers of hydroquinone (HQ) and hexamethylenetetramine (HMT) in a 1:1 weight ratio and aqueous potassium chloride (KCl) solution. A specific amount of the above solution is added to the sand, well mixed, and subsequently cured at 150 °C for 8 h. The prepared super-hydrophilic sands were characterized by Fourier-transform infrared spectroscopy (FT-IR) for chemical composition and X-ray diffraction (XRD) for successful polymer coating onto the sand. The water storage for the samples was studied by absorption kinetics at various temperature conditions, and extended water release was studied by water desorption kinetics. The water swelling ratio for the super-hydrophilic sand has reached a maximum of 900% (9 times its weight) at 80 °C within 1 h. The desorption kinetics of the samples showed that the water can be stored for up to a maximum of 3 days. Therefore, super-hydrophilic sand particles were successfully prepared by coating them with PAM hydrogels, which have great potential to be used in sustainable desert agriculture.

Europium (Eu) doped Calcium borophosphate (CBP) phosphors were synthesized via the solid-state diffusion method. The prepared Europium (Eu) doped Calcium borophosphate (CBP) powder was heated up to 600 ℃ for 6 h for a complete diffusion of ions in the powder system. XRD results showed that the prepared phosphors exhibit a well-crystallized hexagonal phase. The complete diffusion inside the CBP/Eu powder system has been confirmed by the presence of elements such as P, O, Bi, Ca, C, Eu, and B. Apart from that, the synthesized powder system has shown a down-conversion property where the Eu³⁺-activated ion was excited at 251 nm. Under the excitation of 251 nm, CBP/Eu phosphor showed intense emissions peaking at 591,617, and 693 nm due to the ⁵D₀ → ⁷F₁, ⁵D₀ → ⁷F₂, and ⁵D₀ → ⁷F₄ transition of Eu³⁺ ions. The obtained results suggest that the CBP/Eu phosphors have the potential for spectral response coating materials to improve photovoltaic (PV) panel efficiency.

Subcutaneous (SC) drug delivery is one of the best routes of drug administration to patients over intravenous (IV) administration due to the ease of application and patient acceptance. The main limitation of using the SC route is administering larger volumes of drug, greater than 3–5 mL for therapeutic dosages. Wearable injectors on body devices are an attractive option for larger-volume drug delivery to patients. Thus, the need for a self-administration strategy at home is growing faster and is required for the next level of time-dependent and high-volume drug delivery. The advances in low-cost, connected on-body delivery systems hold great opportunity for novel ways of delivering home-based drug therapy in the future.

Disease epidemics may spread quickly and easily throughout nations and continents in our current global environment, having a devastating effect on public health and the world economy. There are over 513 million people worldwide who have been infected, and more than 6.2 million have died due to SARS-CoV-2. There are treatments but no cures for most viruses. Nevertheless, the spread of viruses can be limited by introducing antiviral coatings on public area surfaces and personal protective equipment (e.g., face masks). This work aims to fabricate a polymer-based coating with acrylic resin as a binder that possesses great antiviral activity against the Feline coronavirus (FCov). The chosen polymer, polyethylene glycol (PEG), is used as an antiviral agent because it contains “green” chemistry benefits such as non-toxicity, being inexpensive, readily recyclable, safe, natural, non-flammable, biocompatible, and biodegradable. The PEG/acrylic coating systems of different weight percentages were coated on the glass substrates by the spray-coating method and cured at room temperature for 24 hours. The developed PEG/acrylic coating system that contains 20 wt% of PEG exhibits the highest anti-viral activities (99.9% against FCov) compared to the other weight percentages. From this study, it has been observed that the hydrophilicity of the coating plays an important role in its antiviral activity. The developed coating has a hydrophilic property, in which the contact angle was measured at 83.28 ± 0.5°. The FTIR reveals that there are no existing toxic components or new components contained in the coating samples.

The environmental issue of single-use plastic is extremely discussed due to waste accumulation and the consumption of non-renewable resources. This study aims to investigate the properties of bioplastic compared to petroleum-based plastic. Two stages of stretch blow molding were used to fabricate polyethylene terephthalate (PET) and bio-polyethylene terephthalate (Bio-PET) bottles. The shelf life extension of chili sauce paste stored in PET and Bio-PET containers with an oxygen scavenger at 45 ℃ in an accelerated condition was investigated. After twelve weeks, the chili sauce paste stored in the container bottle was observed. PET and Bio-PET bottles without oxygen scavengers were also determined as a control for comparison. The result showed that both PET and Bio-PET bottles with oxygen scavengers could prolong the quality of chili sauce paste similarly, meaning that PET could be replaced by Bio-PET as a chili sauce paste container. Other properties, such as thickness gauge, color, leak test, drop test, and close-open force of the container bottle, were also verified to check the product quality standard.

Endosulfan (6,7,8,9,10,10-Hexachloro-1,5,5a,6,9,9a-hexahydro-6,9-methano-2,4,3-benzodioxathiepine-3-oxide) is an off-patent insecticide used in agricultural farms. Its usage as a pesticide has become highly controversial over the last few decades. This is due to its reported hazardous nature to health and side effects like growth retardation, hydrocephalus, and undesired changes in the male and female hormones leading to complications in sexual maturity. Endosulfan is the main culprit among all pesticide poisoning incidents around the world. Though the usage of this dreaded pesticide is banned by most countries, the high stability of this molecule to withstand degradation for a long period poses a threat to mankind even today. So, it has become highly essential to detect the presence of this poisonous pesticide in the drinking water and milk around these places. It is also advisable to check the presence of this toxic material in the blood of the population living in and around these places so that an early and appropriate management strategy can be adopted. With this aim, we have developed a sensor for endosulfan that displayed high selectivity and sensitivity among all other common analytes in water and biological samples, with a wide linear concentration range (2 fM to 2 mM), a low detection limit (2 fM), and rapid response. A citrate-functionalized cadmium-selenium quantum dot was used for this purpose, which showed a concentration-dependent fluorescence enhancement, enabling easy and sensitive sensing. This sensor was utilized to detect endosulfan in different sources of water, human blood serum, and milk samples with good recoveries. It is also noted that the quantum dot forms a stable complex with endosulfan and is easy to separate from the contaminated source, paving the way for purifying the contaminated water. More detailed tests and validation of the sensor are needed to confirm these observations.

In the present work, a series of butyl methacrylate/1-hexene copolymers were synthesized, and their efficiency as viscosity index improvers, pour point depressants, and shear stabilizers of lube oil was investigated. The effect of 1-hexene molar ratio, type, and concentration of Lewis acids on the incorporation of 1-hexene into the copolymer backbone was investigated. The successful synthesis of the copolymers was confirmed through FTIR and 1H NMR spectroscopy. Results obtained from quantitative 1H NMR and GPC revealed that an increase in the molar ratio of 1-hexene to butyl methacrylate, along with concentration of Lewis acids led to an increase in 1-hexene incorporation and a reduction in Mn and Ð. Similar trends were observed when the Lewis acid changed from AlCl₃ to organometallic acids. The maximum 1-hexene incorporation (26.4%) was achieved for sample BHY3, with a [1-hexene/BMA] ratio of 4 mol% and a [Yb(OTf)₃/BMA] ratio of 2.5 mol%. Evaluation of the synthesized copolymers as lube oil additives demonstrated that the viscosity index was more significantly influenced by samples with higher molecular weight. Sample BHA13 represents maximum VI of 137. The copolymer containing Yb(OTf)₃ as a catalyst exhibited superior efficiency as a pour point depressant. Furthermore, sample BHY3 showed the lowest shear stability index (6.4).